Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 12, Article number: 17687 (2022 ) Cite this article Manual Lead Door
Aluminosilicates (AS) are ubiquitous in ceramics, geology, and planetary science, and their glassy forms underpin vital technologies used in displays, waveguides, and lasers. In spite of this, the nonequilibrium behavior of the prototypical AS compound, mullite (40SiO2-60Al2O3, or AS60), is not well understood. By deeply supercooling mullite-composition liquid via aerodynamic levitation, we observe metastable liquid–liquid unmixing that yields a transparent two-phase glass, comprising a nanoscale mixture of AS7 and AS62. Extrapolations from X-ray scattering measurements show the AS7 phase is similar to vitreous SiO2 with a few Al species substituted for Si. The AS62 phase is built from a highly polymerized network of 4-, 5-, and 6-coordinated AlOx polyhedra. Polymerization of the AS62 network and the composite morphology provide essential mechanisms for toughening the glass.
Mullite is an eminent material throughout the field of ceramics, from pottery and porcelains to refractories and thermal barrier coatings1. As a phase in the CaO-MgO–Al2O3-SiO2 (CMAS) system, which is present throughout the Universe, it also represents an important geological material, formed at the Earth’s surface when basaltic magmas contact clay minerals2. In the aluminosilicate (AS) binary, the mullite composition (40SiO2-60Al2O3, or AS60) is effectively an endmember of AS-based glasses. These constitute a large fraction of functional glasses due to their hardness and toughness3. A key to obtaining these glasses’ desirable properties is navigating around the system’s metastable liquid–liquid immiscibility during processing, which can lead to phase-separated glasses in the SiO2-rich region of the phase diagram upon melt quenching4. Avoiding or manipulating this immiscibility provides the means to control properties of the resulting glasses.
The known AS miscibility gap ranges qualitatively from near SiO2 and ends prior to the mullite composition, approximately AS7-AS56. Yet, substantial disagreement persists regarding the compositional and temperature limits of immiscibility (Fig. 1). Many experimental studies have located the mullite composition outside the miscibility gap4,5,6, while different thermodynamic models have predicted it within7,8 or outside9,10,11 the gap (see Fig. 1). In this regard, though mullite is ubiquitous in ceramics, its structural role in AS phase separation remains an unsolved mystery. This mainly arises because of the high temperatures involved and the metastable nature of the liquid–liquid phase separation dome, which exists hundreds of degrees below the equilibrium melting point (\({T}_{m}\) ~ 1890 °C for mullite11). Rosales-Sosa et al.12 recently reported a mullite-composition glass with exceptional hardness (8.07 GPa) and crack resistance (55.4 N), which sparks renewed curiosity about the structure of mullite-composition glass and an explanation for these desirable properties. (Hereafter, mullite-composition glass is referred to as “mullite glass,” defined as the glassy form obtained by melt quenching of the AS60 liquid.) Here, we find that mullite glass is in fact two-phase, with nanometer domains of SiO2-rich glass embedded in a glassy, polymerized Al2O3-rich network. Glass structure and electron microscopy measurements provide unambiguous evidence of liquid–liquid phase separation in mullite and provide an experimentally-based estimate for the high-Al2O3 limit of AS immiscibility. Atomic structure modeling of this Al-rich endmember illuminates the structural underpinnings of mullite glass’s excellent crack resistance.
Metastable liquid–liquid immiscibility in SiO2-Al2O3. Numerous locations for the miscibility gap have been proposed based on experimental observations of quenched glasses and thermodynamic calculations (colored curves with Ref. numbers given in figure). The compositional and temperature limits of immiscibility vary substantially between studies, with the Al2O3-rich endmember intersecting \({T}_{g}\) anywhere from 56 to > 85 mol. %. Equilibrium phase diagram adapted from Mao et al.11. Glass transition is \({T}_{g}\) 7, and crystallization of glasses upon heating is \({T}_{x}\) 41.
Because of its reticence to vitrify, mullite-composition glasses are often partially crystalline13,14, and fully glassy materials are typically limited to particle sizes of 10s or 100s of microns, prepared via roller quenching or other techniques that achieve extremely fast cooling (~ 106 °C s−1)1. Here, fully glassy beads, approximately 2 mm in diameter, were prepared using aerodynamic levitation and laser beam heating15, which avoids heterogeneous nucleation while maintaining moderate cooling rates (\(\le\) 103 °C s−1). This is crucial because the fast rates associated with roller quenching have previously obfuscated the full extent of AS phase separation16,17. Phase separation in the glass is evident from ultra-small and small-angle X-ray scattering (Fig. 2A), which exhibits a peak near \(Q\) = 0.05 Å−1, where \(Q\) is the momentum transfer given by \(Q=4\pi \mathrm{sin}(\theta )/\lambda\) and 2 \(\theta\) is the scattering angle. Using Guinier analysis (Fig. 2A inset) and assuming a spherical scatterer, this peak corresponds to domains with a diameter of 5.5 nm. High-angle annular dark field scanning transmission electron microscopy (STEM, Fig. 2B) reveals separated Si-rich domains within an Al-rich matrix, with a domain size of 4–6 nm consistent with the Guinier analysis. From the apparent areal fractions in the STEM image and assuming a Si-rich endmember composition of AS7, based on previous studies7,18,19, the Al-rich endmember phase has a composition of 61.9(7) mol% Al2O3 (~ AS62). This AS62 estimate significantly extends the experimentally-observed immiscibility range beyond the AS56 limit suggested by previous direct observations4,5, and it coincides with the intersection of \({T}_{g}\) with the miscibility gap proposed by Mao et al.11 in their thermodynamic reassessment of the SiO2-Al2O3 system (Fig. 1, purple curve). Despite the phase separation, the mullite glass is optically transparent (Fig. 2B, inset).
Phase separation in mullite-composition glass. (A) X-ray scattering differential cross section exhibits a Porod slope to the right of a small-angle peak near 0.05 Å−1 (gray arrow), indicative of phase-separated domains. Inset: Guinier analysis predicts an average domain size of 5.5 nm. (B) High-angle annular dark field STEM image of a 40–100 nm thick mullite-composition glass specimen, revealing contrast between the 4–6 nm Si-rich domains (black) and surrounding Al-rich matrix. Inset: transparent glass bead, 1.3 mm in diameter.
According to an exhaustive review of phase separation behavior in binary silicate systems by Hudon and Baker20, liquid–liquid separation in aluminosilicates is driven by coulombic repulsions between poorly screened Al3+ cations. In these glasses, Al3+ is an amphoteric cation, referring to its ability to adopt different coordination numbers with oxygen: 4, 5, and 6. The partial covalent character of tetrahedral AlO4 species reduces their electrostatic repulsions with other cations, but the Al3+ in octahedral AlO6 species are poorly screened. To achieve stoichiometric charge balance in the AS binary system, both AlO4 and AlO6 coexist, thus leading to phase separation.
The local atomic structure in mullite glass was probed with high-energy X-ray diffraction and 27Al magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy. For X-ray diffraction, the total structure factor, \(S(Q)\) , is Fourier transformed to obtain the real-space differential pair distribution function (PDF), \(D(r)\) , shown in Fig. 3A (see Supplementary Information S1 (SI) for PDF definitions). The first PDF peak near 1.77 Å comprises overlapping contributions from the Si–O and Al-O atomic partial pair correlations. Fitting Gaussian functions to these peaks and integrating the Al-O peak yields the mean atomic coordination, \({n}_{AlO}\) = 4.38(7). The glass lacks significant local order beyond the second (Si/Al)-O coordination shell, i.e., above 5 Å. The 27Al MAS NMR spectrum (Fig. 3B) contains three overlapping peaks at 67.9, 40.4, and 9.9 ppm, corresponding to AlO4, AlO5, and AlO6 species, respectively14. Using peak shapes guided by separate 27Al triple-quantum MAS (3QMAS) NMR measurements on the same glass (SI, Fig. S1), integration of these peaks yields relative population fractions of 0.498(42), 0.430(41), and 0.072(10), respectively, and a mean coordination of \({n}_{AlO}\) = 4.57(27) consistent with the X-ray analysis. The presence of AlO5 and AlO6 species is also consistent with reports of Raman spectroscopy for Al2O3-rich silicate glasses13,21. The substantial AlO5 fraction, absent in crystalline mullite22, is a structural motif shared in common with the liquid23 that is quenched into the glass structure6.
Average local atomic structure in mullite-composition glass. (A) Differential PDF from high-energy X-ray diffraction. The slope for \(r\) < 1 Å is \(-4\pi \rho\) , with \(\rho\) = 2.912 g cm−3, or 0.08640 atoms Å−3. Gaussian functions were fit for the weighted Si–O and Al-O partial pair correlations. (B) The 27Al MAS NMR spectrum exhibits three peaks corresponding to different Al speciation.
To gain further structural insights, experimentally-constrained models for the phase-separated endmembers are sought. X-ray diffraction interference functions, \(Q(S\left(Q\right)-1)\) , were measured for compositions AS12-AS61 (Fig. 4A), spanning the immiscibility range. These glasses are each phase-separated into the same endmembers, whose relative fractions vary linearly with glass composition. The interference functions were therefore extrapolated24 to predict the interference functions for the AS7 and AS62 endmembers (Fig. 4B), for which atomistic models were obtained by Empirical Potential Structure Refinement (EPSR)25.
Structure of the endmembers in phase-separated mullite and aluminosilicate glasses. (A) X-ray diffraction interference functions of phase-separated glasses, with compositions ranging AS12-AS61. (B) Interference functions for the endmember compositions, AS7 and AS62, linearly extrapolated from the glasses in (A). EPSR provides structural models of the endmembers consistent with the experimental data: (C) structure visualizations, (D) oxygen coordination environments, and (E) ring size distributions of AS7 and AS62 endmembers. \({R}_{c}\) is the number of -O-(Si/Al)- rings normalized by the number of atoms in the simulation volume.
The structure of AS7 (Fig. 4C) is similar to that of SiO2 glass: O atoms are 93% bridging (i.e., connecting two (Si/Al)Ox polyhedra), 5% form triclusters26 (Fig. 4D), and the network comprises 99% corner-sharing between polyhedra that form rings with a distribution modal size of 7 cations (Fig. 4E). In contrast, the AS62 structure contains 60% O as triclusters, making it much more topologically rigid27. Oxygen triclusters are a charge balancing mechanism20 and here are associated with Al-rich environments such as O-Al3 and O-SiAl2. While substantial, this large tricluster fraction is consistent with molecular dynamics (MD) simulations for mullite glass28 and is reasonable in comparison to MD predictions of 82% triclusters in melt quenched Al2O329. The AS62 network contains a mixture of AlOx species: 57% 4-, 37% 5-, and 6% 6-coordinate. These polyhedra and the SiO4 are connected via 86% corner- and 13% edge-sharing, forming more than 3 \(\times\) the number of rings as compared to AS7. This large number of rings makes AS62 highly polymerized.
Nanoscale phase separation and atomic structure are the keys to understanding AS glasses’ trend of increasing hardness—and, anomalously, crack resistance—with Al2O3 content12. For a single phase, hardness is proportional to density12, so the higher density of AS62 leads to higher hardness compared to AS7. For any glass composition within the miscibility gap, the glass comprises domains of the two endmember phases, AS7 and AS62, with relative volume fractions that are linearly dependent on composition. This linear dependence of the volume fractions explains the linear relationship of hardness with increasing Al2O3 content. This trend also matches the linear increase of O triclusters (SI, Fig. S2A), which topologically harden the atomic network. Cracking resistance (CR) in glass is often attributed to the availability of free volume to accommodate plastic deformation, so CR typically decreases with density, yet the opposite is observed for the AS compositional series. Rosales-Sosa et al. hypothesized this is due to rearrangement of the multiple AlOx environments, enabling shear deformation12, which is supported by the low energy barrier predicted by MD for AlO5 configurational transitions in AS glasses30.
The discovery of phase separation in mullite glass and the structure of the Al-rich endmember point to two additional CR mechanisms. First, the highly polymerized network in AS62 makes it more difficult to form cavities that lead to crack formation, according to MD simulations of high- and low-brittleness single-phase AS glasses under mechanical loading31. These simulations also showed that cracking is mitigated by the breaking of larger rings (containing ~ 6 cations) into 3- and 4-member rings, so the much larger population of rings in AS62 is supportive of its higher CR compared to AS7. Second, CR has been observed to increase nonlinearly with Al2O3 content: from 8 to 20 N for AS30 to AS55, then jumping to 55 N for AS6012. This jump can be explained by the relative fractions and morphologies of the phase-separated domains. As Al2O3 content increases from AS55 to AS60, the more easily-cracked AS7 phase becomes sufficiently disconnected (Fig. 2B) such that cracks can no longer propagate continuously through AS7, so the more crack-resistant AS62 matrix thus suddenly increases CR.
Commercial glasses can be toughened by surface modification (e.g., ion exchange32) and/or by creating a composite structure that results in crack deflection (e.g., in glass-ceramics33). This work shows the potential for using phase-separated vitreous materials. The presence of a highly polymerized network and the composite nature of the two-phase glass offer additional design approaches in the toolbox for glass strengthening. Combination of techniques, for example, selective ion exchange of only one phase in a separated glass, may open up new possibilities. Though mullite is a reluctant glass former, its ~ 390 °C difference between \({T}_{g}\) and \({T}_{x}\) (Fig. 1) suggests it could be formed in thin sheets, where cooling rates are sufficiently high and heterogeneous nucleation can be avoided.
Full information on the experimental methods is provided in the SI.
Glass beads were prepared from mixtures of SiO2 and Al6Si2O13 powders using aerodynamic levitation and heating with a 10.6 μm CO2 laser beam15. Nominal compositions of 10, 20, 30, 35, 40, 50, and 60 mol. % Al2O3 (AS10-AS60) were heated to 2000 °C and then cooled at rates < 103 °C s−1 to obtain colorless, transparent glass beads 1.5–2 mm in diameter. Evaporation of SiO2 caused 2–10% mass loss during melt processing, resulting in final compositions consistent with energy dispersive spectroscopy on polished cross-sections: AS12, 23, 33, 38, 42, 54, and 61. For the mullite glass (AS61), annular dark field STEM images were collected at 200 keV beam energy. Specimens were prepared by in situ lift-out from a glass cross-section, followed by ion beam thinning at 5 keV. The composition of the Al2O3-rich endmember was estimated to be 61.9(7) mol. % Al2O3, or ~ AS62, from the areal fractions observed in STEM, assuming a SiO2-rich endmember composition of AS77,18,19.
27Al MAS NMR spectroscopy was conducted at an external field strength of 16.4 T, spinning at 22 kHz, and referenced to an external shift standard of aqueous aluminum nitrate at 0.0 ppm. Data were processed with VnmrJ and DMFit softwares, using the Czjzek function to represent each of the three resonances34. The quadrupolar coupling constant, isotropic chemical shift, and peak areas were extracted from peak fits35. 27Al 3QMAS NMR data were collected using standard two-pulse experiments with a z-filter, and analyses of these data were used to further guide fitting of the 27Al MAS NMR data.
X-ray scattering measurements were collected for the ultra-small and small-angle range with 21 keV X-rays36, as well as the small- and wide-angle range with 60 keV X-rays37. For PDF analysis, dedicated wide-angle scattering (100 keV) data were reduced to obtain the total structure factors and then Fourier transformed to obtain the PDFs38. Mean bond distances and coordinations for Si–O and Al-O were extracted from the PDFs with Gaussian peak fits39. Structure factors for glasses in the AS12-AS42 compositional range were extrapolated to estimate the structure factors for the AS7 and AS62 phase-separated endmembers. Structural models for AS7 and AS62 were created using EPSR25, a Monte Carlo based technique that perturbs a system with known composition, density, and simple interatomic potentials, to optimize agreement between the experimental and simulated scattering. Atomic coordination distributions and ring statistics40 were calculated from these models.
All data are available upon reasonable request from the corresponding author. Structure factor data are provided in the SI for the X-ray diffraction measurements.
Schneider, H. & Komarneni, S. Mullite (Wiley-VCH, 2005).
Bowen, N. L., Greig, J. W. & Zies, E. G. Mullite, a silicate of alumina. J. Washingt. Acad. Sci. 14, 183–191 (1924).
Kohli, J. T., Hubert, M., Youngman, R. E. & Morse, D. L. A Corning perspective on the future of technical glass in our evolving world. Int. J. Appl. Glas. Sci. 13, 292–307 (2022).
MacDowell, J. F. & Beall, G. H. Immiscibility and crystallization in Al2O3-SiO2 glasses. J. Am. Ceram. Soc. 52, 17–25 (1969).
Risbud, S. H. & Pask, J. A. Mullite crystallization from SiO2-Al2O3 melts. J. Am. Ceram. Soc. 61, 63–67 (1978).
Poe, B. T., McMillan, P. F., Angell, C. A. & Sato, R. K. Al and Si coordination in SiO2-Al2O3 glasses and liquids: A study by NMR and IR spectroscopy and MD simulations. Chem. Geol. 96, 333–349 (1992).
Article ADS CAS Google Scholar
Risbud, S. H. & Pask, J. A. Calculated thermodynamic data and metastable immiscibility in the system SiO2-Al2O3. J. Am. Ceram. Soc. 60, 418–424 (1977).
Djuric, M., Mihajlov, A., Petrasinovic-Stojkanovic, L. & Zivanovic, B. Thermodynamic analysis of the metastable regions for the Al2O3-SiO2 system. J. Am. Ceram. Soc. 79, 1252–1256 (1996).
Ban, T., Hayashi, S., Yasumori, A. & Okada, K. Calculation of metastable immiscibility region in the Al2O3–SiO2 system. J. Mater. Res. 11, 1421–1427 (1996).
Article ADS CAS Google Scholar
Takei, T., Kameshima, Y., Yasumori, A. & Okada, K. Calculation of metastable immiscibility region in the Al2O3-SiO2 system using molecular dynamics simulation. J. Mater. Res. 15, 186–193 (2000).
Article ADS CAS Google Scholar
Mao, H., Selleby, M. & Sundman, B. Phase equilibria and thermodynamics in the Al2O3-SiO2 system—Modeling of mullite and liquid. J. Am. Ceram. Soc. 88, 2544–2551 (2005).
Rosales-Sosa, G. A., Masuno, A., Higo, Y. & Inoue, H. Crack-resistant Al2O3-SiO2 glasses. Sci. Rep. 6, 23620 (2016).
Article ADS CAS Google Scholar
Okuno, M., Zotov, N., Schmücker, M. & Schneider, H. Structure of SiO2–Al2O3 glasses: Combined X-ray diffraction, IR and Raman studies. J. Non. Cryst. Solids 351, 1032–1038 (2005).
Article ADS CAS Google Scholar
Weber, R., Sen, S., Youngman, R. E., Hart, R. T. & Benmore, C. J. Structure of high alumina content Al2O3-SiO2 composition glasses. J. Phys. Chem. B 112, 16726–16733 (2008).
Weber, J. K. R. The containerless synthesis of glass. Int. J. Appl. Glas. Sci. 1, 248–256 (2010).
Jantzen, C., Schwahn, D. & Schelten, J. Phase Decomposition in Al2O3-SiO2 Glasses. J. Appl. Cryst. 11, 614–615 (1978).
Risbud, S. H. & Pask, J. A. On the location of metastable immiscibility in the system SiO2-Al2O3. J. Am. Ceram. Soc. 62, 214–215 (1978).
Nassau, K., Shiever, J. W. & Krause, J. T. Preparation and properties of fused silica containing alumina. J. Am. Ceram. Soc. 58, 461 (1975).
Sen, S. & Youngman, R. E. High-resolution multinuclear NMR structural study of binary aluminosilicate and other related glasses. J. Phys. Chem. B 108, 7557–7564 (2004).
Hudon, P. & Baker, D. R. The nature of phase separation in binary oxide melts and glasses. I. Silicate systems. J. Non. Cryst. Solids 303, 299–345 (2002).
McMillan, P. & Piriou, B. The structures and vibrational spectra of crystals and glasses in the silica-alumina system. J. Non. Cryst. Solids 53, 279–298 (1982).
Article ADS CAS Google Scholar
Rehak, P. et al. Study of the Al coordination in mullites with varying Al: Si ratio by 27Al NMR spectroscopy and X-ray diffraction. Am. Mineral. 83, 1266–1276 (1998).
Article ADS CAS Google Scholar
Krishnan, S., Weber, J. R. K., Ansell, S., Hixson, A. D. & Nordine, P. C. Structure of Liquid Al6Si2O13 (3:2 Mullite). J. Am. Ceram. Soc. 83, 2777–2780 (2000).
Soper, A. K., & Ricci, M. A. Structures of high-density and low-density water. Phys. Rev. Lett. 84, 2881 (2000).
Soper, A. K. Empirical potential Monte Carlo simulation of fluid structure. Chem. Phys. 202, 295–306 (1996).
Stebbins, J. F. & Xu, Z. NMR evidence for excess non-bridging oxygen in an aluminosilicate glass. Nature 390, 60–62 (1997).
Article ADS CAS Google Scholar
Welch, R. S. et al. Topological hardening through oxygen triclusters in calcium aluminosilicate glasses. J. Am. Ceram. Soc. 104, 6183–6193 (2021).
Liao, K. et al. Real-space mapping of oxygen coordination in phase-separated aluminosilicate glass: Implication for glass stability. ACS Appl. Nano Mater. 3, 5053–5060 (2020).
Shi, C. et al. The structure of amorphous and deeply supercooled liquid alumina. Front. Mater. 6, 1–15 (2019).
Article ADS CAS Google Scholar
Wiles, N. T., Goyal, S. & Baker, S. P. Geometric configuration of five-coordinated Al and Si in tectosilicate calcium aluminosilicate glasses and its effect on plastic flow. J. Non. Cryst. Solids 543, 120129 (2020).
Ito, S. Structural study on mechanical behavior of glass. J. Ceram. Soc. Japan 112, 477–485 (2004).
Beall, G. H. et al. Ion-exchange in glass-ceramics. Front. Mater. 3, 41 (2016).
Okuma, G., Maeda, K., Yoshida, S., Takeuchi, A. & Wakai, F. Morphology of subsurface cracks induced by Vickers indentation observed by synchrotron X-ray multiscale tomography. Sci. Rep. 12, 6994 (2022).
Article ADS CAS Google Scholar
Massiot, D. et al. Modelling one- and two-dimensional solid-state NMR spectra. Magn. Reson. Chem. 40, 70–76 (2002).
Neuville, D. R., Cormier, L. & Massiot, D. Al environment in tectosilicate and peraluminous glasses: A 27Al MQ-MAS NMR, Raman, and XANES investigation. Geochim. Cosmochim. Acta 68, 5071–5079 (2004).
Article ADS CAS Google Scholar
Ilavsky, J. et al. Development of combined microstructure and structure characterization facility for in situ and operando studies at the Advanced Photon Source. J. Appl. Crystallogr. 51, 867–882 (2018).
Benmore, C. J. et al. Extended range X-ray pair distribution functions. Nucl. Instruments Methods Phys. Res. Sect. A Accel. Spectrometers, Detect. Assoc. Equip. 955, 163318 (2020).
Benmore, C. J. A review of high-energy X-ray diffraction from glasses and liquids. ISRN Mater. Sci. 2012, 1–19 (2012).
Pickup, D., Moss, R. & Newport, R. NXFit: A program for simultaneously fitting X-ray and neutron diffraction pair-distribution functions to provide optimized structural parameters. J. Appl. Crystallogr. 47, 1790–1796 (2014).
Le Roux, S. & Jund, P. Ring statistics analysis of topological networks: New approach and application to amorphous GeS2 and SiO2 systems. Comput. Mater. Sci. 49, 70–83 (2010).
Takamori, T. & Roy, R. Rapid Crystallization of SiO2-Al2O3 glasses. J. Am. Ceram. Soc. 56, 639–644 (1973).
This research was funded by the National Aeronautics and Space Administration (NASA), grant 80NSSC18K0059. X-ray scattering measurements were made at Sectors 6-ID-D and 9-ID-C of the Advanced Photon Source, a U.S. DOE Office of Science User Facility, operated by Argonne National Laboratory under Contract No. DE-AC02-06CH11357. SEM/EDS measurements were made at the EPIC Facility of Northwestern University’s NUANCE Center, which has received support from the SHyNE Resource (NSF ECCS-2025633), the IIN, and Northwestern's MRSEC program (NSF DMR-1720139).
Materials Development, Inc., Evanston, IL, 60202, USA
Stephen K. Wilke, Vrishank Menon & Richard Weber
X-Ray Science Division, Advanced Photon Source, Argonne National Laboratory, Argonne, IL, 60439, USA
Stephen K. Wilke, Chris J. Benmore, Jan Ilavsky & Richard Weber
Science and Technology Division, Corning Incorporated, Corning, NY, 14831, USA
Randall E. Youngman, Aram Rezikyan & Michael P. Carson
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
Conceptualization: C.J.B., R.W. Formal analysis: S.K.W., C.J.B., J.I., R.E.Y., R.W. Funding acquisition: R.W. Investigation: S.K.W., C.J.B., J.I., R.E.Y., A.R., M.P.C., V.M., R.W. Visualization: S.K.W. Writing—original draft: S.K.W. Writing—review and editing: S.K.W., C.J.B., J.I., R.E.Y., A.R., R.W.
Correspondence to Stephen K. Wilke.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Wilke, S.K., Benmore, C.J., Ilavsky, J. et al. Phase separation in mullite-composition glass. Sci Rep 12, 17687 (2022). https://doi.org/10.1038/s41598-022-22557-7
DOI: https://doi.org/10.1038/s41598-022-22557-7
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
Protective Lead Apron Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.